| MOQ: | 100 KGS |
| Prijs: | USD16.45/KG |
| Standaardverpakking: | Houten doos |
| Leveringstermijn: | 7 dagen |
| Betaalmethode: | L/C, T/T |
| Toeleveringskapaciteit: | 50000 KGS |
| Normen | Staalsoorten | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Chemische samenstelling % | ||||||||||
| C: | Monometers | Si: | P: | S: | Cr: | Ni: | Mo: | Cu: | N: | |
| Vervaardiging | X1NiCrMoCuN25-20-7 - X1CrNiMoCuN25-20-7 - 1.4529 | |||||||||
| < 0.02 | < 1.0 | < 0.5 | < 0.03 | < 0.01 | 19.0 tot 21.0 | 24.0 - 26.0 | 6.0 tot en met 7.0 | 0.5 tot 1.5 | 0.10-0.25 | |
| ASTM | UNS N08926 - 26-3 Mo - 6 Mo - legering 926 | |||||||||
| < 0.02 | < 2.0 | < 0.5 | < 0.03 | < 0.01 | 19.0 tot 21.0 | 24.0 - 26.0 | 6.0 tot en met 7.0 | 0.5 tot 1.5 | 0.15 - 0.25 | |
| ASTM | N08925 van de VN | |||||||||
| < 0.02 | < 1.0 | < 0.5 | < 0.045 | < 0.03 | 19.0 tot 21.0 | 24.0 - 26.0 | 6.0 tot en met 7.0 | 0.8 tegen 1.5 | 0.1 - 0.2 | |
| SUS | 317 J5L | |||||||||
| < 0.02 | < 2.0 | < 1.0 | < 0.045 | < 0.03 | 19.0 - 23.0 | 23.0 - 28.0 | 4.0 tot en met 5.0 | 1.0 tot 2.0 | - | |
1.4529 is hoog gelegeerd roestvrij staal met een austenitische structuur, dat kan worden ingedeeld als nikkellegeringen (volgens Amerikaanse normen).
Leverbaar in superverzadigde staat, weerstand tegen interkristallijn, pitting en stress corrosie, zout, zeewater, chloride, zwavelzuur,fosforzuur en andere agressieve chemische stoffen in hoge concentraties in vloeibare en gasvormige vorm.
Materialen van de kwaliteit 1.4529, met uitzondering van chemische bestandheid, kunnen bij hoge temperaturen werken met behoud van adequate mechanische eigenschappen.
Met het oog op het hoge gehalte aan nikkel en chroom wordt in de norm ook een relatief grote hoeveelheid molybdeen en stikstof gespecificeerd.die vooral nuttig is bij het selecteren van een kwaliteit uit de bijbehorende groep van hooggelegeerde staal.
Een aanzienlijk hoger percentage stikstof en molybdeen draagt bij tot de beperking van de vorming van intermetalen fasen en tot een betere slagweerstand.
Staal wordt hoofdzakelijk gebruikt in de chemische, papieren, cryogene, lucht- en ruimtevaart- en energie-industrie.schachten, waterontzilting en ontzwaveling van rookgassen, kleppen en zelfs radiatorcomponenten.
| Eigenschappen | Werktemperatuur | |||||
|---|---|---|---|---|---|---|
| 100°C | 200°C | 300°C | 400°C | 500°C | ||
| Het rendementpunt, Rp0,2 | MPa | > 230 | >190 | > 170 | > 160 | - |
| Lineaire uitbreidingsfactor, α | * 10-6K-1 | 15,8 | 16,1 | 16,5 | 16,9 | 17,3 |
| Elastiekmodulus,E | GPa | 190 | 182 | 174 | 166 | 158 |
|
|
| MOQ: | 100 KGS |
| Prijs: | USD16.45/KG |
| Standaardverpakking: | Houten doos |
| Leveringstermijn: | 7 dagen |
| Betaalmethode: | L/C, T/T |
| Toeleveringskapaciteit: | 50000 KGS |
| Normen | Staalsoorten | |||||||||
|---|---|---|---|---|---|---|---|---|---|---|
| Chemische samenstelling % | ||||||||||
| C: | Monometers | Si: | P: | S: | Cr: | Ni: | Mo: | Cu: | N: | |
| Vervaardiging | X1NiCrMoCuN25-20-7 - X1CrNiMoCuN25-20-7 - 1.4529 | |||||||||
| < 0.02 | < 1.0 | < 0.5 | < 0.03 | < 0.01 | 19.0 tot 21.0 | 24.0 - 26.0 | 6.0 tot en met 7.0 | 0.5 tot 1.5 | 0.10-0.25 | |
| ASTM | UNS N08926 - 26-3 Mo - 6 Mo - legering 926 | |||||||||
| < 0.02 | < 2.0 | < 0.5 | < 0.03 | < 0.01 | 19.0 tot 21.0 | 24.0 - 26.0 | 6.0 tot en met 7.0 | 0.5 tot 1.5 | 0.15 - 0.25 | |
| ASTM | N08925 van de VN | |||||||||
| < 0.02 | < 1.0 | < 0.5 | < 0.045 | < 0.03 | 19.0 tot 21.0 | 24.0 - 26.0 | 6.0 tot en met 7.0 | 0.8 tegen 1.5 | 0.1 - 0.2 | |
| SUS | 317 J5L | |||||||||
| < 0.02 | < 2.0 | < 1.0 | < 0.045 | < 0.03 | 19.0 - 23.0 | 23.0 - 28.0 | 4.0 tot en met 5.0 | 1.0 tot 2.0 | - | |
1.4529 is hoog gelegeerd roestvrij staal met een austenitische structuur, dat kan worden ingedeeld als nikkellegeringen (volgens Amerikaanse normen).
Leverbaar in superverzadigde staat, weerstand tegen interkristallijn, pitting en stress corrosie, zout, zeewater, chloride, zwavelzuur,fosforzuur en andere agressieve chemische stoffen in hoge concentraties in vloeibare en gasvormige vorm.
Materialen van de kwaliteit 1.4529, met uitzondering van chemische bestandheid, kunnen bij hoge temperaturen werken met behoud van adequate mechanische eigenschappen.
Met het oog op het hoge gehalte aan nikkel en chroom wordt in de norm ook een relatief grote hoeveelheid molybdeen en stikstof gespecificeerd.die vooral nuttig is bij het selecteren van een kwaliteit uit de bijbehorende groep van hooggelegeerde staal.
Een aanzienlijk hoger percentage stikstof en molybdeen draagt bij tot de beperking van de vorming van intermetalen fasen en tot een betere slagweerstand.
Staal wordt hoofdzakelijk gebruikt in de chemische, papieren, cryogene, lucht- en ruimtevaart- en energie-industrie.schachten, waterontzilting en ontzwaveling van rookgassen, kleppen en zelfs radiatorcomponenten.
| Eigenschappen | Werktemperatuur | |||||
|---|---|---|---|---|---|---|
| 100°C | 200°C | 300°C | 400°C | 500°C | ||
| Het rendementpunt, Rp0,2 | MPa | > 230 | >190 | > 170 | > 160 | - |
| Lineaire uitbreidingsfactor, α | * 10-6K-1 | 15,8 | 16,1 | 16,5 | 16,9 | 17,3 |
| Elastiekmodulus,E | GPa | 190 | 182 | 174 | 166 | 158 |